The rate of crystallization of Polyethylene terephthalate) (PET) can be improved by blending it with polyethylene co chlorotrifluoroethylene) (ECTFE; tradename Halar) so that it can be suitable for injection molding. The special advantage of this method is that molecular weight of the blend will not decrease so much as by adding nucleating agents. That is to say, the mechanical strength of the blend will not decrease very much compared with that of virgin PET.